Henan Jixiang Industry Co., Ltd; Henan Aludong Decorative Materials Co.,Ltd is located in Zhengzhou City,Henan Province, Which a professional enterprise manufacturing high and new-tech aluminum composite products,which is one of the earliest and scaled manufacturers of aluminum composite, coated aluminum coils, aluminum solid panel in China.Our company possesses16 production lines and 6 coating lines for aluminum composite panels whose annual output is 5.8million square meters.In addition, our company has passed ISO9001 International Quality Management System Certification, ISO14000 Environment Management System Certification, OHSAS18000 Occupation Health Safety Management System Certification, and CTC Product Quality Certification, and won several national patents.
Aluminum composite panel (ACP) is made of aluminum alloy and plastic material provided with wide range of sizes, shapes, colors, and styles to offer broader options for construction design, in a bid to better meet the requirements of contemporary construction on lightweight, elegant decoration and high hardness.
Base material: High strength aluminum alloy sheet
PE core material: Non - toxic low density polyethylene
Surface coating: high performance polyester coating
Back coating: Polyester coating or primer
Special advantages that distinguish this product from ordinary aluminium plastic panels.
Dimensional Tolerance:
Panel width: +-2mm
Panel length: +-3mm
Panel thickness: +-0.2mm
Panel diagonal: <5mm
Aluminum sheet thickness: +-0.02mm
Applications:
| ALUDONG Technical data for Polyester Coating: |
| Description | Test standard | Polyester |
| Coating Thickness (μm) | Polyester paint >=16μm | 16μm to 18μm |
| Coating flexibility (T-bend) | Polyester paint ≤ 3T | ≤ 3T |
| Color different | ΔE<=2.0 (follow color sample) | ΔE<=2.0 |
| Pencil hardness | >=HB | >=2H |
| Chemical resistance | 2%HCI or 2%NaOH test in 24 hours -No change | No change |
| Coating adhesion | >=1grade for 10810mm2 gridding test | 1grade |
| Resist solvent | 100 times without change | No change |
| Boiling water resistance | 2 hours without change | No change |
| Peeling strength/stripping strength | Average >=5N/mm of 180oc peel off for panel with 0.21mm alu.skin | 5N/mm |
| Impact test for paint | 20KG.cm impact-paint no split for panel | No split |
| Abrasion resistance (L/Mil) | NIL | NIL |
| Temperature resistance | -40ºC to +80ºC temperature without change of color differenceand paint peel off , peeling strength average dropprate<=10% | Change of glossy only, no paint Peel off |
| Coefficient of linear Thermal Expansion | 100ºC temperature difference | 2.4mm/n |
| Detergent resistance (3%) | ASTM D2248 | No change |
| Humidity Resistance | ASTM D2247 (2000hrs,100%RH,100°F) | No change |
| Salt spray resistance | ASTM B117 (2000hrs,2% salt) | No change |
| Resistance to Staining | 600h radiate in 800W/M2 in humidity condition,glossiness deviation less grade 2,color difference <=4.0 | No change |
ALUDONG Technical data for PVDF Coating:
| Description | Test standard | PVDF |
| Coating Thickness (μm) | Polyester paint >=25μm | 26μm |
| Coating flexibility (T-bend) | Polyester paint ≤ 3T | ≤ 2T |
| Color different | ΔE<=2.0 (follow color sample) | ΔE<=2.0 |
| Pencil hardness | >=HB | >=2H |
| Chemical resistance | 5%HCI or 5%NaOH test in 48 hours -No change | No change |
| Coating adhesion | >=1grade for 10810mm2 gridding test | 1grade |
| Resist solvent | 100 times without change | No change |
| Boiling water resistance | 2 hours without change | No change |
| Peeling strength/stripping strength | Average >=5N/mm of 180oc peel off for panel with 0.30mm alu.skin | 5N/mm |
| Impact test for paint | 50KG.cm impact-paint no split for panel | No split |
| Abrasion resistance (L/Mil) | NIL | NIL |
| Temperature resistance | -40ºC to +80ºC temperature without change of color differenceand paint peel off , peeling strength average dropprate<=10% | Change of glossy only, no paint Peel off |
| Coefficient of linear Thermal Expansion | 100ºC temperature difference | 2.4mm/n |
| Detergent resistance (3%) | ASTM D2248 | No change |
| Humidity Resistance | ASTM D2247 (3000hrs,100%RH,100°F) | No change |
| Salt spray resistance | ASTM B117 (3000hrs,5% salt) | No change |
| Resistance to Staining | 600h radiate in 800W/M2 in humidity condition,glossiness deviation less grade 2,color difference <=4.0 | No change |